High Alumina Insulation JM23 Mullite Refractory Brick
High alumina lightweight insulation mullite refractory brick JM23 is a kind of quality refractory insulation materials for resisting high temperature with features of light weight, low thermal conductivity, thermal insulation and high compression strength in the high temperature furnaces or kilns. lightweight bricks are mainly used for the top of hot blast stove, stack and bottom of blast furnace, regenerative chamber of glass melting furnace, lining of ceramic high temperature furnace and so on.
lightweight brick is manufactured with mullite as the main crystal phase and contains about 65~75% alumina content. Mullite Insulation Refractory Brick has high refractoriness that reaches up to 1790 ℃. Its apparent initial softening temperature is about 1600~1700 ℃. Its cold crushing strength is about 70~260MPa.
Mullite Insulation Refractory Brick can be classified into different types of 1350 lightweight brick, 1450 lightweight brick and 1550 lightweight brick according to different service temperature and into Lightweight Mullite Brick and Heavy Mullite Brick according to different bulk density.
Features:
High alumina lightweight insulation mullite refractory brick is a kind of quality high temperature materials with the following excellent performance:
Low thermal conductivity and Low heat capacity
High Purity and low impurity content
Excellent high temperature strength
Good thermal shock resistance
Low expansive conductivity
Great resistance to acid and alkali erosion
High alumina lightweight insulation mullite refractory brick JM23:
1. Excellent compression strength
2. Excellent heat stability
3. Low thermal conductivity
4. Low heat storage
5. High alumina, low iron and alkali flux content
6. Accurate dimension
7. designed packaging
| Item | DLG180-1.5L | DLG170-1.3L | LG160-0.8L | LG150-0.8L | LG140-0.7L | LG125-0.5L | |
| Al2O3 % | ≥90 | ≥72 | ≥60 | ≥55 | ≥50 | ≥48 | |
| Fe2O3 % | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | |
| Bulk Density ( g/cm3) | ≤1.5 | ≤1.3 | ≤1.0 | ≤0.8 | ≤0.7 | ≤0.5 | |
| Cold Crushing Strength (MPa) | ≥9.5 | ≥5.0 | ≥3.0 | ≥2.5 | ≥2.0 | ≥1.5 | |
| Linear Change on Reheating | ≤1% | 1800 | 1700 | 1600 | 1500 | - | - |
| ≤2% | - | - | - | - | 1400 | 1250 | |
| Thermal conductivity(350±25)℃ (W/mK) | ≤0.8 | ≤0.6 | ≤0.4 | ≤0.35 | ≤0.3 | ≤0.2 | |